PENGARUH PENGGUNAAN SEMEN PPC (PORTLAND POZOLAND CEMENT) DENGAN FAS 0,4 TERHADAP KUAT TEKAN, MODULUS ELASTISITAS, DAN SERAPAN AIR PADA BETON.

Abstract

Penelitian ini menggunakan metode penelitian eksperimen. Pada penelitian ini dilakukan uji kuat tekan pada beton umur 3, 7, 14, 28, 60, dan 90 hari. Serta uji modulus elastisitas dan serapan air pada beton umur 28, 60, dan 90 hari. Benda uji kuat tekan modulus elastisitas beton adalah sampel silider dengan diameter 150 mm dan tinggi 300 mm. Sedangkan pengujian serapan air beton digunakan benda uji kubus dengan panjang sisi 150 mm.Dari hasil penelitian didapatkan hasil kuat tekan semakin meningkat seiring bertambahnya umur beton yaitu 13,079 MPa, 17,723 MPa, 23,017 MPa, 28,036 MPa, 31,611 MPa, dan 33,679 MPa pada umur 3, 7, 14, 28, 60, dan 90 hari. Pada tegangan maksimum, regangan beton diperoleh sekitar 0,002. Modulus elastitas beton di dapatkan nilai E = 4420√fc’. Serta di dapat nilai modulus elastisitas yang semakin meningkat seiring besarnya kuat tekan beton dan bertambahnya umur, yaitu sebesar 21.215,7 MPa; 21.822 MPa; 24.537 MPa pada umur 28, 60, dan 90 hari. Sedangkan Serapan air pada beton dengan fas 0,4 menghasilkan nilai serapan air sebesar 3,49%; 2,05%; 0,64% terhadap berat kering oven untuk umur 28, 60, dan 90 hari. Disimpulkan bahwa beton yang menggunakan semen PPC dengan fas 0,4 menghasilkan kuat tekan maksimal pada umur 28 hari adalah 28,036 MPa. Dan nilai modulus elastisitas yang didapat E = 4420√fc’ dengan nilai maksimal pada umur 28 hari sebesar 21.822 MPa. Serta serapan air sebesar 3,49% pada umur 28 hari.

 

This study uses experimental research. In this research, concrete compressive strength test at the age of 3, 7, 14, 28, 60, and 90 days. Test and modulus of elasticity and water absorption in concrete ages 28, 60, and 90 days. Compressive strength of the specimen modulus of elasticity of concrete is sampled cylinder with a diameter of 150 mm and height 300 mm. While the water absorption test specimen used concrete cube with side length of 150 mm.From the results, the results of the compressive strength of concrete increases with age ie 13,079 MPa, 17,723 MPa, 23,017 MPa, 28,036 MPa, 31,611 MPa and 33,679 MPa at the age of 3, 7, 14, 28, 60, and 90 days. At the maximum stress, the concrete strain is obtained around 0.002. Elastitas concrete modulus value E = 4420√fc get. As well as can the value of the elastic modulus increase as the concrete compressive strength and age, that is equal to 21215.7 MPa; 21 822 MPa; 24 537 MPa at 28, 60, and 90 days. While Absorption of water on the concrete with water/cement ratio 0.4 produce water absorption value of 3.49%; 2.05%; 0.64% of the dry weight of the oven for ages 28, 60, and 90 days.Concluded that the concrete using PPC cement with water/cement ratio 0.4 of generate maximum compressive strength at 28 days was 28,036 MPa. And modulus of elasticity values obtained E = 4420√fc 'with a maximum value at 28 days was 21 822 MPa. And water absorption of 3.49% at 28 days.