The Effect of Bentonite Powder as a Filler on HRS-WC Asphalt Performance
DOI:
https://doi.org/10.15294/jtsp.v27i1/8133Keywords:
Wearing Course Lataston, Filler, Bentonite PowderAbstract
Wearing Course Lataston (HRS-WC) is a type of flexible pavement with durable and good durability and flexibility. The constituent materials of HRS-WC asphalt consist of aggregate, asphalt, and filler. Bentonite powder is an active chemical filler material with superior swelling ability, ion exchange properties, and large surface area. It quickly absorbs water to form a thick suspension. This research aims to determine and determine the Optimum Asphalt Content (OAC), optimum filler content, comparison of the percentage value of increase or decrease in Marshall test parameters, and the effect of adding bentonite powder filler to HRS-WC Asphalt on asphalt performance according to the General Specifications for Bina Marga Year 2018 Revision 2. Based on the research results on Marshall characteristics, the KAO value was obtained at 7.5%, and the optimum filler content value was 1.90%. The addition of bentonite filler shows changes in the characteristics of HRS-WC asphalt, namely an increase in stability, Marshall Quotient, and VFA, as well as a decrease in flow, VIM, and VMA. So, the effect of adding bentonite filler to HRS-WC asphalt can increase density, reduce the number of voids, fill voids between aggregates, and be able to bind asphalt to the asphalt mixture. However, the excessive addition of bentonite powder as a filler can reduce the flow value and make the asphalt mixture harder and stiffer.
Downloads
References
A. Rezi and M. Allam, "Techniques in array processing using transformations, " in Control and Dynamic Systems, Vol. 69, Multidimensional Systems, C. T. Leondes, Ed. San Diego: Academic Press, 1995, pp. 133-180.
Utomo, N., Wahjudijanto, I., & Sri Rizki Yasin, F. (2020). Penggunaan Limbah Serbuk Besi Sebagai Material Pengisi (Filler) Pada Campuran Struktur Perkerasan Jalan Kolektor Ponco – Jatirogo. Jurnal Environtek, 12(2), 64–74.
Sholichin, I., & Sutama, D. A. (2019). Variations in adding polypropylene fiber, fly ash, and immersion in asphalt mixtures on stability and flow. International Journal of Civil Engineering and Technology, 10(2), 2032–2039.
Direktorat Jenderal Bina Marga. (2018). Spesifikasi Umum 2018 Untuk Pekerjaan Konstruksi Jalan dan Jemabatan (Revisi 2). Surat Edaran Dirjen Bina Marga. Nomor 16.1/SE/Db/2020.
Manoppo, M. R. E. (2011). Pemanfaatan Tras Sebagai Filler Dalam Campuran Aspal Panas HRS-WC. Jurnal Ilmiah MEDIA ENGINEERING, 1(2), 2087–9334.
Bukit, F. R. A., Frida, E., Bukit, N., & Bukit, B. (2021). Karakteristik dan Analisis Bentonit Alam Sebagai Bahan Pengisi Komposit. Juitech, 5(2), 54–62.
Ibnu, A. R. (2023). Analisis Pengaruh Pengganti Filler dengan Bentonit Terhadap Kinerja Perkerasana Aspal [Teknik Sipil, Universitas Muhammadiyah Sumatera Utara]. Dalam Tugas Akhir Teknik Sipil, Universitas Muhammadiyah Sumatera Utara.
Ruskandi, C., Siswanto, A., & Widodo, R. (2020a). Karakterisasi fisik dan kimiawi bentonite untuk membedakan natural sodium bentonite dengan sodium bentonite hasil aktivasi. Jurnal Polimesin, 18(1), 53–61.
Nur Khaerat Nur, & dkk. (2021). Perancangan Perkerasan Jalan (1 ed.). Yayasan Kita Menulis
L. Hendarsin, S. (2000). Penuntun Praktis Perencanaan Teknik Jalan Raya (1st ed.). Politeknik Negeri Bandung - Jurusan Teknik Sipil.
Nahyo, Sudarno, & Hario Setiadji, B. (2015). Durabilitas Campuran Hot Rolled Sheet-Wearing Course ( HRS-WC ) Akibat Rendaman Menerus dan Berkalan Air Rob. 13(1), 124–135.
Buchari, & Harsini, M. (1996). Karakteristik Bentonite Pacitan. JKTI, 6(1–2), 43–48.
Linggo, J. S., & Purnamasari, P. E. (2007). Pengaruh Serat Serabut Kelapa Sebagai Bahan Tambah dengan Filler Serbuk Bentonit Pada HRS-Base dan HRS-WC. Jurnal Teknik Sipil, 7(3), 236–252.
Sugatama, N., Sriharyani, L., & Hadijah, I. (2022). Desain Perkerasan Jalan Raya. JUMATISI, 3(2), 250–255.
Winarno, B., Catur Budi, K., Sumargono, Iwan Candra, A., Muslimin, S., & Sudjati. (2020). Pengaruh Abu Batu Sebagai Filler Terhadap Kinerja Aspal Beton AC-WC Pada Test Marshall. Jurnal Civilla, 5(2), 468–475.