MODEL KUAT TEKAN, POROSITAS DAN KETAHANAN AUS PROPORSI LIMBAH PELEBURAN BESI DAN SEMEN UNTUK BAHAN DASAR PAVING BLOCK

Moch. Husni Dermawan

Abstract


Abstract: Utilization of iron smelting waste has not been fully utilized for building materials, especially as an ingredient in the manufacture of paving block stacking. The purpose of this study was to characterize the slag and to determine compressive strength, porosity, wear resistance of paving blocks by using slag as a sand substitute. The method used by experimental methods. Preparation of specimens made 2 types of test object without slag and specimens with slag content. The specimens made 4 treatment research slag content of 20%, 40%, 60%, and 80%. Each group was made of samples, 5 for compressive strength, 5 porosity and 5 wear resistance. Testing is done at BPIK Semarang. Test results from block paving with slag content of 0% shows the compressive strength of 204.24 kg / cm ², 4.95% porosity, resilience auas 0.145 mm / min. Slag content of 20%, compressive strength of 192.13 kg / cm ², 6.150% porosity, wear resistance 0.186 mm / min. Slag content of 40%, compressive strength of 179.33 kg / cm ², 7.657% porosity, wear resistance 0.259 rnm / min. Slag content of 60%, compressive strength of 164.94 kg / cm ², 8.509% porosity, wear resistance 0.3482. 80% slag content of compressive strength of 149.06 kg / cm ², 9.911% porosity, wear resistance 0.448 mm / min. Compressive strength of paving blocks with slag content of 20% and 40% belong to the quality of III, the porosity of the paving block 20% slag content is categorized in the quality of III, and wear resistance of paving blocks slag content of 20%belong to the quality of III.

Keywords: compressive strength, wear resistance, porosity, paving block

 

Abstrak: Pemanfaatan limbah peleburan besi belum dimanfaatkan secara maksimal untuk bahan bangunan, khususnya sebagai bahan susun dalam pembuatan paving block. Tujuan dalam penelitian ini adalah untuk mengetahui karakteristik terak dan untuk mengetahui kuat tekan, porositas, ketahanan aus paving block dengan menggunakan terak sebagai bahan substitusi pasir. Metode yang digunakan dengan metode eksperimen. Pembuatan benda uji dibuat 2 jenis yaitu benda uji tanpa terak dan benda uji dengan kandungan terak. Benda uji penelitian dibuat 4 perlakuan kandungan terak yaitu 20%, 40%, 60%, dan  80%. Tiap kelompok dibuat benda uji, 5 untuk kuat tekan, 5 porositas dan 5 ketahanan aus. Pengujian dilakukan di BPIK Semarang. Hasil pengujian dari paving block dengan kandungan terak 0% menunjukkan kuat tekan 204,24 kg/cm², porositas 4,95%, ketahanan auas 0,145 mm/menit. Kandungan terak 20%, kuat tekan 192,13 kg/cm², porositas 6,150%, ketahanan aus 0,186 mm/menit. Kandungan terak 40%, kuat tekan 179,33 kg/cm², porositas 7,657%, ketahana aus 0,259 rnm/menit. Kandungan terak 60%, kuat tekan 164,94 kg/cm², porositas 8,509%, ketahanan aus 0,3482. Kandungan 80% terak kuat tekan 149,06 kg/cm², porositas 9,911%, ketahanan aus 0,448 mm/menit. Kuat tekan paving block dengan kandungan terak 20% dan 40% tergolong dalam mutu III, porositas paving block kandungan terak 20% tergolong dalam mutu III, dan ketahanan aus paving block kandungan terak 20% tergolong dalam mutu III.

Kata Kunci: kuat tekan, keausan, porositas, paving block


Keywords


compressive strength; wear resistance; porosity; paving bloc; kuat tekan; keausan; porositas

Full Text:

PDF PostScript

References


Anonim. 1980. Standar Cara-Cara Pengujian Dan Syarat Mutu Ubin Semen. Buletin Informasi Bahan Bangunan 1:1:22-25.

Anonim. 1987. Ubin Semen (SNI-03-0028-J987). Bandung: Departemen Pekerjaan Umum, Yayasan Lembaga Penyclidikan Masalah Bangunan.

Anonim. 1989. Bata Beton Untuk Lantai (SNI-03-0691-1989). Bandung: Departemen Pekerjaan Umum, Yayasan Lembaga Penyelidikan Masalah Bangunan.

Anonim. 1991. Tata Cara Perhitungan Struktur Beton Untuk Bangunan Gedung (SKSNI-T-J 5-1990-03). Bandung: Departemen Pekerjaan Umum, Yayasan Lembaga Penyelidikan Masalah Bangunan.

Anonim. 1995. Petunjuk Praktek Asislen Teknisi Laboratorium Pengujian Beton, Bandung : Pusat Pelatihan MBT.

Endah Salmi. 2001. Daya Serap Radiasi Neotron Sepat Dan Sinar Gama Dan Sifat Mekanis Beton Semen Polimer Dengan Agregat Slag Baja. Thesis. Yogyakarta: Program Pasca Sarjana UGM.

Istiwarni. 2002. Analisa Paving Block Dan Limbah Karbit, Skripsi. Yogyakarta: Universitas Negeri Yogyakarta.

Joni Talu Lembang, dkk. 1990. Pemanfaatan Limbah Slag Peleburan Logam Sebagai Agregat Pada Pembuatan Bala Beton Kuat Tekan Tinggi. Ujung Pandang: Badan Penelitian Dan Pengembangan Industri.

Nadhiroh Masruri. 1992. Penelitian Pemanfaatan Limbah Industri Peleburan Timah Untuk Bahan Bangunan. Jurnal Penelitian Pemukiman I. VII: 43-51.

Silvia Sukirman. 1994. Dasar-Dasar Perencanaan Geometrik Jalan. Bandung : Nova. Tjokrodimuljo. 1998. Teknologi Beton. Yogyakarta: Naviri.




DOI: https://doi.org/10.15294/jtsp.v13i1.1325

Refbacks

  • There are currently no refbacks.