AN ANALYSIS OF METAL SURFACE IMMERSED IN BASED LUBRICANT FROM MINERAL OIL CONTAINING VEGETABLE OIL WITH RICE BRAN OIL BASED BIO-INHIBITOR
Abstract
The need for environmentally friendly chemical products in daily needs encourages the production of its. The green-chemistry concept is using the process and produces chemical products that are ecofriendly. Including ecofriendly chemical products are base oil and additives for lubricants, grease, and fuels. The production is expected to reduce the consumption of mineral and synthetic base oils, so it will be biodegradable and renewable. This study compares the results of analysis of metallic surfaces immersed in the mixture of mineral and vegetable base oil, with the addition of rice bran oil bioadditive, ie epoxidized methyl ester (EME) and hydroxyl alkylbenzene sulphonic acid ester (HASE). The research method consists of preparing HASE; analyzing the effect of HASE and EME bioadditives addition on the mixture of base oil to the changing of metallic weight immersed in the mixture; determining the inhibition efficiency of the EME and HSAE additions; analyzing the metal surface using SEM-EDX (Scanning Electron Microscope) / (Energy Dispersive X-ray Spectrometry) to find images of microstructure and chemical compounds contained in specimens, and testing the metal difractogram immersed in base oil mixtures with bioadditive using XRD (X-Ray Diffraction). SEM test results of carbon steel immersed in a mixture of base oil and bioadditives show corrosion in which the metal surface color immersed in EME bioadditive mixtures is brighter. EDX spectra of metal sample surfaces immersed in a mixture of base oil, EME and HASE contain carbon (C) and iron (Fe). The carbon content in carbon steel samples immersed in the mixtures and HASE is higher. XRD test results show Fe2O3 phases in carbon steel samples immersed in the HASE bioadditive mixture are higher than in EME. While Fe3O4 phases in carbon steel samples immersed in the EME bioadditive mixture are higher than Fe2O3 phases in samples immersed in HASE bioadditive mixture.
Keywords
Full Text:
PDFReferences
Adhvaryu, A., Sharma, B.K., Erhan, Z.S. 2005. Current Developments of Biodegradable Grease, Industrial Uses of Vegetable Oils. Chapter 2. Champaign, IL: AOCS Press. 14-30.
Aini, N., Triwikantoro, T., Pengaruh Konsentrasi Air dalam Pelumas terhadap Sifat Korosi Baja Karbon ST 37, http://digilib.its.ac.id/public/ITS-Undergraduate-23787-Paper 856382.pdf
Al-Sabagh, A. M., Abd El-Bary, H. M., El-Ghazawy, R. A., Mishrif. M. R., Hussein, B. M. 2012. Corrosion inhibition efficiency of heavy alkyl benzene derivatives for carbon steel pipelines in 1 M HCl. Egyptian Journal of Petroleum. 21(2): 89-100.
Anbarasi, M., Rajendran, M., Pandiarajan, M., Krishnaveni, A. 2013. An Encounter with Corrosion Inhibitors. European Chemical Bulletin. 2(4): 197-207.
Azlina, N., Ali M., 2010. Production of high temperature grease using spent bleaching earth (sbe). Thesis. Faculty of Chemical & Natural Resources Engineering. University Malaysia Pahang.
Bayuseno, A. P., Handoko, E. D. 2012. Analisa Korosi Erosi Pada Baja Karbon Rendah dan Baja Karbon Sedang Akibat Aliran Air Laut. Thesis. Jurusan Teknik Mesin Universitas Diponegoro.
Coupland, K., Smith, C.R. 1981. Hydrocarbon-soluble epoxidized fatty acid esters as lubricity modifiers for lubricating oils. Paten US 4244829
Dermawan, D., Pertiwi, D. S., Siddik, A., Pahlevi, S.R. 2011. Pengembangan Minyak Lumas Biobased: Formulasi Dengan Ashless Antiwear Agent, Prosiding Seminar Rekayasa Kimia Dan Proses.
Dermawan, D., Pertiwi, D. S., Normalita, N. H., Virgyni, T., 2012, Pengembangan Minyak Lumas Bio-Based: Efek Sinergistik Senyawa Molybdenum Pada Peningkatan Sifat Tekanan Ekstrem, Prosiding SNTK TOPI.
Farooq, M., Ramli, A., Gul, S., Muhammad, N. 2011. The Study of Wear Behaviour of 12-hydroxystearic Acid in Vegetable Oils. Journal of Applied Science. 11 (7): 1381-1385.
Finger, L. W., Hazen R. M. 1980. Crystal structure and isothermal compression of Fe2O3, Cr2O3, and V2O3 to 50 kbars. Journal of Applied Physics. 51: 5362-5367
Gatta G. D., Kantor I., Ballaran T. B., Dubrovinsky L., McCammon C. 2007. Effect of nonhydrostatic conditions on the elastic behaviour of magnetite: an in situ single-crystal X-ray diffraction study Locality: synthetic Sample: P = 4.99 GPa, T = 293 K. Physics and Chemistry of Minerals. 34: 627-635.
Holser, R. A. 2008. Transesterification of epoxidized soybean oil to prepare epoxy methyl esters, Industrial Crops and Products. 27(1): 130–132
Kumpawat, N., Chaturvedi, A., Upadhyay, R. K. 2012. Comparative Study of Corrosion Inhibition Efficiency of Naturrally Occuring Ecoriendly Varieties of Holy Basil (Tulsi) for Tin in HNO3 Solution. Iranian Journal of Materials Science and Engineering. 10(4): 43 – 48.
Nugrahani, R. A., Redjeki, A. S., Teresa, Y., Hidayati, N. 2016. Effect of Linear Alkylbenzene Sulphonate on Oxirane Oxygen of Epoxidized Rice Bran Oil Methyl Ester. Proceedings The 2nd International Multidiciplinary Conference, Universitas Muhammadiyah Jakarta, Indonesia. 425-431.
Nugrahani, R. A., Redjeki, A. S., Teresa, Y., Hidayati, N. 2017. Synthesis of Compound-Containing Sulphonic Acid of Epoxidized Methyl Oleic of Rice Bran Oil and Linear Alkyl Benzene Sulphonic Acid. Journal of Chemical Technology and Metallurgy. 52(5): 797-802
Ningsih, T. D., Farida, R., Nugrahani, R. A. 2017. Pengaruh Blending Minyak Nabati pada Pelumas dari Minyak Mineral terhadap Stabilitas Oksidasi dan Ketahanan Korosi Logam. Jurnal Konversi. 6(1): 7 -12.
Rowland, R., Migdal, C. 2006. Epoxidized ester additives for reducing lead corrosion in lubricants and fuels. Patent US Application 20060090393 (Patent WO 2006049687 A1).
Schafer, V., Kohler, R., Pauli, A., Fessenbecker, A. 1994. Corrosion protection additives based on epoxides. Patent US 5368776 A.
Refbacks
- There are currently no refbacks.